US Patent Issued to BAOSHAN IRON & STEEL on Feb. 3 for "Low-carbon, low-alloy and high-formability dual-phase steel having tensile strength of greater than or equal to 590 MPa, hot-dip galvanized dual-phase steel, and manufacturing method therefor" (Chinese Inventors)

ALEXANDRIA, Va., Feb. 3 -- United States Patent no. 12,540,365, issued on Feb. 3, was assigned to BAOSHAN IRON & STEEL Co. LTD. (Shanghai).

"Low-carbon, low-alloy and high-formability dual-phase steel having tensile strength of greater than or equal to 590 MPa, hot-dip galvanized dual-phase steel, and manufacturing method therefor" was invented by Jun Li (Shanghai), Jian Wang (Shanghai), Junfei Wang (Shanghai), Chao Wang (Shanghai), Baoping Zhang (Shanghai), Huafei Liu (Shanghai), Jingge Dai (Shanghai), Yimin Liu (Shanghai), Fengzhi Lu (Shanghai) and Honglin Yang (Shanghai).

According to the abstract* released by the U.S. Patent & Trademark Office: "A low-carbon, low-alloy and high-formability dual-phase steel having a tensile strength of...